Nanocrystalline Ni-Cr
New Xtalic nanocrystalline Nickel-Chrome (Ni-Cr) alloys are engineered to reduce oxidation-based corrosion at temperatures up to 900°C — delivering a significant advantage to supplant the use of commercial Nickel (Ni) in many applications.
Comparing commercial Ni to our new nanocrystalline Ni-Cr alloy for hot oxidation performance at 700°C for 20 hours, the commercial Ni oxidizes quickly to create a thick oxide layer of 1.35um. In contrast, in the Xtalic nanocrystalline Ni-Cr alloy, the Cr selectively oxidizes at the surface to produce a thinner (0.30um) and protective chromium oxide layer on the surface.
[fusion_builder_container hundred_percent=”yes” overflow=”visible”][fusion_builder_row][fusion_builder_column type=”1_1″ background_position=”left top” background_color=”” border_size=”” border_color=”” border_style=”solid” spacing=”yes” background_image=”” background_repeat=”no-repeat” padding=”” margin_top=”0px” margin_bottom=”0px” class=”” id=”” animation_type=”” animation_speed=”0.3″ animation_direction=”left” hide_on_mobile=”no” center_content=”no” min_height=”none”]
Our new nanocrystalline Ni-Cr alloys reduce corrosion at temperatures up to 900°C
In a wide variety of applications, new Xtalic Ni-Cr alloys are well suited to replace commercial Ni to both improve performance and reduce corrosion.[/fusion_builder_column][/fusion_builder_row][/fusion_builder_container]